Bambu Lab Filament PLA Basic Orange 1kg, 28.50 CHF

Bambu PLA Basic 1kg

If you are just getting started with 3D printing, then PLA (Polylactic Acid) the filament is the best choice.
PLA is usually the first filament used by beginners in 3D printing, as it is expected to have relatively predictable results. But PLA isn’t only for beginners.
Many manufacturers and designers use it for prototyping and tooling. PLA is the default filament of choice for most extrusion-based 3D printers because it can be printed at a low temperature and does not require a heated bed.
It is also one of the most environmentally friendly filaments on the market today. Derived from crops such as corn and sugarcane, PLA is renewable and biodegradable. As a bonus, this also gives the plastic a sweet aroma during printing.
Most PLA filaments don't suffer from moisture absorption, but it is still recommended to keep the filaments away from humid environments.
In summary, for beginner 3D printing, switching to other types of material is not recommended until you are confident with PLA.

New-user Friendly & Easy to Print
Bambu PLA Basic is designed to be extremely user-friendly, making it an ideal choice for beginners or those new to 3D printing. What’s more, PLA Basic enables users to achieve high-quality prints consistently, without the need for extensive adjustments or advanced printing settings.

High-printing Quality
Bambu Lab's PLA filament stands out for its high print speed, and excellent appearance. Experience the benefits of smooth and flawless prints with superior quality that exceeds expectations.

RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.

Recommended Printing Settings
Drying Settings (Blast Drying Oven)	55 °C，8 h
Printing and Keeping Container's Humidity	< 20% RH (Sealed, with Desiccant)
Nozzle Temperature	190 - 230 °C
Bed Temperature (with Glue)	35 - 45 °C
Printing Speed	< 300 mm/s
Physical Properties
Density	1.24 g/cm³
Vicat Softening Temperature	57 °C
Heat Deflection Temperature	57 °C
Melting Temperature	160 °C
Melt Index	42.4 ± 3.5 g/10 min
Mechanical Properties
Tensile Strength	35 ± 4 MPa
Breaking Elongation Rate	12.2 ± 1.8 %
Bending Modulus	2750 ± 160 MPa
Bending Strength	76 ± 5 MPa
Impact Strength	26.6 ± 2.8 kJ/m²