VALUE LINE Tough (ABS Like) 1.0L white, 52.90 CHF

Description
Reviews

Value Line UV/DLP Tough (ABS Like) 1.0L white

When you want astonishing results for less cost than many other brands - PrimaCreator VALUE resin should be your first choice!

Resin from our VALUE line is a high-quality resin made from the best materials.
Your prints cures in sunlight or a UV curing chamber. When the curing is finished, the result is a rock-hard print with very small shrinkage and ABS – like

The finished print is a solid color part with a beautiful matte surface with excellent details and smooth layer transitions.
Tough (ABS like) resin has the added benefit of being much more flexible and stronger than normal resin. It´s also less brittle which means that it can be bent and still go back to its original shape.
Tough resin is perfect for model making as it´s easy to post process. This resin is also very suitable for functional prototyping as it is tough enough to be handled, glasses is a great example of a product that must be strong but pliable.

VALUE resin is developed to perform well on low powered DLP machines such as the Wanhao Duplicator 7, SparkMaker Anycubic Photon, Zortrax Inkspire and other printers that uses UV light for curing.

Optimized for UV Lightsource 395 – 405 nm.

Fast curing time, 4 – 10 (depending on color) seconds per layer for quicker prints.
After printing clean you print in IPA (Isopropyl Alcohol) to rinse of extra resin left.

When it´s time for curing you can use sunlight or a uv curing chamber.
Depending on print the curing times can vary:

In a UV light curing chamber, it will take about 2-5 minutes.
In sunlight, 10-20 minutes.
In daylight on a cloudy day it can take up to 60 minutes.

Specification:

Flexural modulus	1.192 - 2.525 MPa
Flexural strength	60 - 80 MPa
Thermal expansion	97*E-6
Tensile strength	42-62 MPa
Tensile modulus	1.86 - 2.645 MPa
Elongation at break	11% - 21%
Hardness (Shore D)	76 - 80D
Glass transition temp.	70℃
Density	1.05 - 1.25g/cm3
Notched impact strength	60 - 80j/m
Viscosity	150 - 350 MPa·s
Curing time	4 - 12s for layer thickness 0.05 mm Bottom layer 40 - 60 s